Grade | TF-0956 |
| 树脂种类 | HI-PMMA |
| Home Appliances |
| 项目 | 测试方法 | 条件 | 单位 | 代表值 |
|---|
| 物理性质 | ||||
|---|---|---|---|---|
| 比重 | ASTM D792 | Natural 或代表 color | - | 1.07 |
| 熔融指数 | ASTM D1238 | 220℃, 10kg | g/10min | 6 |
| 熔融指数 | ASTM D1238 | 230℃, 3.8kg | g/10min | 3 |
| 成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.3-0.37 |
| 成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.35-0.42 |
| 机械性质 | ||||
|---|---|---|---|---|
| 拉伸强度(at yield) | ASTM D638 | 5mm/min | kgf/cm2 | 520 |
| 伸长率(at break) | ASTM D638 | 5mm/min | % | 50 |
| 拉伸模量22500 | ASTM D638 | 5mm/min | kgf/cm2 | 22500 |
| 断裂强度(at break) | ASTM D638 | 5mm/min | kgf/cm2 | 460 |
| 弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 750 |
| 弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 20000 |
| Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 4.5 |
| Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 5 |
| 硬度 | ASTM D785 | R-Scale | - | 115 |
| 铅笔硬度 | JIS K 5401 | 500g | - | H |
| 热学特性 | ||||
|---|---|---|---|---|
| 热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 80 |
| 维卡软化温度 | ISO 306 | B/50 | °C | 93 |
| 阻燃 | ||||
|---|---|---|---|---|
| 阻燃度 | UL94 | HB | mm | 1.5,3.0 |
1. 上述数值为NP基准代表值，根据不同颜色可能会有偏差，仅限适用于选定材料为目的
2. 上述数值为选定材料的基础指导，不作为材料正式规格，不适用于模具设计
3. 上述数值可根据实际加工条件进行适当调整和使用，使用范围即最终成品不出现异常状态为止