Grade | CF-1001T |
| 树脂种类 | PC |
| Mobile Devices |
| 项目 | 测试方法 | 条件 | 单位 | 代表值 |
|---|
| 物理性质 | ||||
|---|---|---|---|---|
| 比重 | ASTM D792 | Natural 或代表 color | - | 1.22 |
| 熔融指数 | ASTM D1238 | 250℃, 10kg | g/10min | 95 |
| 熔融指数 | ASTM D1238 | 250℃, 5kg | g/10min | 45 |
| 成型收缩率(MD) | ASTM D955 | Flow at 3.2mm(MD) | % | 0.35-0.42 |
| 成型收缩率(TD) | ASTM D955 | X-Flow at 3.2mm(TD) | % | 0.37-0.45 |
| 机械性质 | ||||
|---|---|---|---|---|
| 拉伸强度(at yield) | ASTM D638 | 50mm/min | kgf/cm2 | 700 |
| 伸长率(at break) | ASTM D638 | 50mm/min | % | 97 |
| 拉伸模量25200 | ASTM D638 | 50mm/min | kgf/cm2 | 25200 |
| 断裂强度(at break) | ASTM D638 | 50mm/min | kgf/cm2 | 650 |
| 弯曲强度 | ASTM D790 | 2.8mm/min | kgf/cm2 | 1000 |
| 弯曲模量 | ASTM D790 | 2.8mm/min | kgf/cm2 | 26500 |
| Izod冲击强度(notched) | ASTM D256 | 1/4 inch at 23°C | kgf·cm/cm | 5 |
| Izod冲击强度(notched) | ASTM D256 | 1/8 inch at 23°C | kgf·cm/cm | 4 |
| 硬度 | ASTM D785 | R-Scale | - | 124 |
| 热学特性 | ||||
|---|---|---|---|---|
| 热变形温度 | ASTM D648 | 18.56kgf/cm2, 6.4mm | °C | 97 |
| 维卡软化温度 | ISO 306 | B/50 | °C | 105 |
| 光学性质 | ||||
|---|---|---|---|---|
| 透過率 | ASTM D1003 | 2mm | % | 89 |
| Haze | ASTM D1003 | 2mm | % | 0.6 |